Elite Engineering is a major Manufacturer and Supplier of Gunmetal Bushes. These Gunmetal Bushes are made using high grade raw materials and according to the international quality standards. Gunmetal is a kind of bronze, which is an alloy of copper, tin and some zinc that is basically used for making guns. It is also known as red brass in America. Gunmetal is produced for various applications that vary slightly in composition. In some cases, the alloy may be composed only from copper and tin, or copper, tin and lead. It has multiple uses in industry and is also applied for statues and various small objects e.g. Gears, Bushes. The Gunmetal Bushes are designed in accordance with the specifications provided by the customers. The range of Gunmetal Bushes is used in many industries which are resistant to rust and durable in nature. These Gunmetal Bushes are offered to our clients at economical prices in the market.
Gunmetal casts and machines well and is resistant to corrosion from steam and salt water, and isused to make steam and hydraulic castings, turned parts, Bushings, Plugs, Threaded connectors, TankConnectors, Water tank DZR Brass fittings, valves, pump parts and gears, and also statues andvarious small objects, e.g. buttons. A material with excellent machining characteristics, good casting qualities and moderate strength. Particularly suitable where pressure tightness is required. It has a tensile strength of 221 to 310 MPa, a specific gravity of 8.7, a density 8,719 kg/m3, and a Brinellhardness of 65 to 74.Main alloys used in Gunmetal castings are -LG2, LG3, LG4, PB, LPB, HTB.
|GRADE BSS / ISS||NOMINAL COMPOSITION [Cu / TIN / Zn / Pb]|
|BS1400 G1-C / ISS 306 Grade I||88 / 10 / 2|
|BS1400 G2-C / ISS 306 Grade II||88 / 8 / 4|
|BS1400 G3-C||85 / 7 / 2.5 / Ni 5.5|
|BS1400 LG1-C||83 / 3 / 9 / 5|
|BS1400 LG2-C / ISS 318 LTB 2||85 / 5 / 5 / 5|
|BS1400 LG3-C/ ISS 318 Grade 1||86 / 7 / 5 / 2|
|BS1400 LG4-C / ISS 318 LTB 1||88 / 7 / 2 / 3|
Most economic and widely used bearing material. Good wear and sliding properties. Due to high lead content good machinability.